This study aims to deal with both the development and mechanical investigations of unsaturated polyester matrix (UPR) composites containing recycled polyethylene terephthalate (PET) fibers as new fillers.

UPR/PET fibers composites have been developed as mats by incorporating 5, 8, 13 and 18 parts per hundred of rubber (phr) of 6-, 10- and 15-mm length PET fibers from the recycling of postconsumer bottles. The mechanical and physical properties of the composites were investigated as a function of fiber content and length. A significant increase in stress at break and in ultimate stress (sr) were observed for composites reinforced with 5 and 8 phr of 15-mm length PET fibers. The Izod impact strength of UPR/mat PET fiber composites as a function of fiber rate and length showed that the 5 and 8 phr composites for the 15-mm length PET fiber have the optimal mechanical properties 13.55 and 10.50 Kj/m², respectively. The morphological study showed that the strong adhesion resulting from the affinity of the PET fiber for the UPR matrix. The ductile fracture of materials reinforced with 5 and 8 phr is confirmed by the fiber deformation and fracture surface roughness.

This study concluded that the PET fiber enhances the properties of composites, a good correlation was observed between the results of the mechanical tests and the structural analysis revealing that for the lower concentrations, the PET fibers are well dispersed into the resin, but entanglements are evidenced when the fiber content increases.

It can be shown from scanning electron microscopy micrographs that the fabrication technique produced composites with good interfacial adhesion between PET fibers and UPR matrix.

This paper aims to design a composite, aiming to improve the static puncture resistance through polyurethane impregnated treatment with five concentration gradients.

The relationship between polyurethane concentration, the number of polyester nonwovens, component fiber type (filament or staple) and the static puncture resistance is explored respectively and elaborately.

This study provides a new perspective to design flexible composites with better static puncture resistance, feasible preparation process as well as low cost.

The results show that the static puncture resistance of nonwovens impregnated by polyurethane is improved obviously. Meanwhile the puncture strength-T of nonwovens increases first and then decreases with the increase of the number of layers, and the maximum puncture strength-T is found at 20 layers. Moreover, the composite with filaments illustrates better mechanical resistance.

This study aims to examine the reuse of plastic and fly ash (FA) to improve the soil and achieve sustainable development goals.

Sand from the Anzali port was reinforced with Geopet (GP) and stabilized with FA plus 3% sodium hydroxide. The GP was placed in FA-stabilized soil and the California bearing ratio (CBR), and unconfined compressive strength (UCS) tests were performed on samples at the optimum moisture content.

The results showed that the improvement in the optimum CBR was 174.9%. The UCS increased 15.25% and 48.65% in soil reinforced with three layers of GP plus 15% FA over those containing 10% and 5% FA, respectively. Additionally, the current analysis used response surface methodology (RSM) to investigate the impact of FA percentage, GP layers and their interaction on CBR. The results highlight the efficacy of the used RSM model, as evidenced by the significantly low p-value (<0.0001).

This demonstrates the suitability and effectiveness of RSM for evaluating CBR in this scientific study.

Polyethylene terephthalate (PET) as a fiber molding polymer is widely used in aerospace, electrical and electronic, clothing and other fields. The purpose of this study is to improve the thermal insulation performance of polyethylene terephthalate (PET), the SiO₂ aerogel/PET composites slices and fibers were prepared, and the effects of the SiO₂ aerogel on the morphology, structure, crystallization property and thermal conductivity of the SiO₂ aerogel/PET composites slices and their fibers were systematically investigated.

The mass ratio of purified terephthalic acid and ethylene glycol was selected as 1:1.5, which was premixed with Sb₂O₃ and the corresponding mass of SiO₂ aerogel, and SiO₂ aerogel/PET composites were prepared by direct esterification and in-situ polymerization. The SiO₂ aerogel/PET composite fibers were prepared by melt-spinning method.

The results showed that the SiO₂ aerogel was uniformly dispersed in the PET matrix. The thermal insulation coefficient of PET was significantly reduced by the addition of SiO₂ aerogel, and the thermal conductivity of the 1.0 Wt.% SiO₂ aerogel/PET composites was reduced by 75.74 mW/(m · K) compared to the pure PET. The thermal conductivity of the 0.8 Wt.% SiO₂ aerogel/PET composite fiber was reduced by 46.06% compared to the pure PET fiber. The crystallinity and flame-retardant coefficient of the SiO₂ aerogel/PET composite fibers showed an increasing trend with the addition of SiO₂ aerogel.

The SiO₂ aerogel/PET composite slices and their fibers have good thermal insulation properties and exhibit good potential for application in the field of thermal insulation, such as warm clothes. In today’s society where the energy crisis is becoming increasingly serious, improving the thermal insulation performance of PET to reduce energy loss will be of great significance to alleviate the energy crisis.

In this study, SiO₂ aerogel/PET composite slices and their fibers were prepared by an in situ polymerization process, which solved the problem of difficult dispersion of nanoparticles in the matrix and the thermal conductivity of PET significantly reduced.

Silicone softeners are widely used in the textile industry to improve the performance of textile products. The thermal characteristics and flammability of polyester fabrics can be influenced by these compounds, which need to be considered, as important issues of human safety. The purpose of this paper is to investigate the changes induced on the polyester fibre by silicone softener treatment using a pad/dry/cure method.

The fibres were first treated with nano‐ and microemulsion silicone softeners. The influence of the silicone emulsion type on thermal properties and flammability of the resultant samples were investigated by various analytical techniques, namely, the differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA), dynamical mechanical thermal analysis (DMTA) and horizontal flammability test (HFT).

Results showed that the silicone softeners increase the thermal degradation and flammability of the polyethylene terephthalate (PET) substrate.

The paper's study of thermal and flammability of the silicone‐treated sample is novel and can be used to optimize the properties of silicone polymers during production and consumption.

The purpose of this study is to improve the mechanical properties, thermal insulation properties and flame retardant properties of polyethylene terephthalate (PET), the organic montmorillonite (OMMT)/SiO₂ aerogel/PET composites and fibers were prepared, and the effects of the OMMT/SiO₂ aerogel on the structure, thermal conductivity and flame retardance of the OMMT/SiO₂ aerogel/PET composites and their fibers were systematically investigated.

The OMMT/SiO₂ aerogel/PET composites and fibers were prepared by in-situ polymerization and melt spinning using SiO₂ aerogel as thermal insulation filler and OMMT (DK2) as comodified filler.

The experimental results showed that OMMT improved the crystallization properties of PET. Compared with the crystallinity of SiO₂ aerogel/PET composites (34.8%), SiO₂ aerogel/PET composites and their fibers reached 45.1% and 49.2%, respectively. The breaking strength of the OMMT/SiO₂ aerogel/PET composite fibers were gradually increased with the OMMT content. When the content of OMMT was 0.8 wt.%, the fracture strength of the composite fibers reached 4.40 cN/dtex, which was 54% higher than that of the SiO₂ aerogel/PET fiber. In addition, the thermal insulation properties of the composites and their fibers were improved by addition of fillers, and at the same time reached the flame retardant level. The thermal conductivity of the 0.8 wt.% OMMT/SiO₂ aerogel/PET composites was 101.78 mW/(m·K), which was 49.3% and 58.8% lower than that of the SiO₂ aerogel/PET composites and the pure PET, respectively. The thermal conductivity of the fiber fabrics woven from the 0.8 wt.% OMMT/SiO₂ aerogel/PET composites was 28.18 mW/(m·K), which was 29.0% and 44.6% lower than that of the SiO₂ aerogel/PET composite fiber fabrics and PET fiber fabrics. The flame retardancy of the composites was improved, with an limiting oxygen index value of 29.2% for the 0.8 wt.% OMMT/SiO₂ aerogel/PET composites, which was 4.1% higher compared to the SiO₂ aerogel/PET composites, and achieved the flame retardant level.

The SiO₂ aerogel/PET composites and their fibers have good mechanical properties, flame retardant properties and thermal insulation properties, exhibited good potential for application in the field of thermal insulation, such as warm clothing. Nowadays, as the energy crisis is becoming more and more serious, it is very important to improve the thermal insulation properties of PET to reduce energy losses and mitigate the energy crisis.

In this study, PET based composites and their fibers with excellent mechanical properties, thermal insulation properties and flame retardant property were obtained by using three-dimensional network porous silica aerogel with low density and low thermal conductivity as the thermal insulation functional filler and two-dimensional layered OMMT as the synergetic modified filler.

The purpose of this paper is to clarify the relationship between the use of different polymer matrices for the preparation of composite materials, namely, polyethylene terephthalate-glycol (PET-G) and polyamide (PA), using Composite Fiber Co-Extrusion technology with the application of two types of carbon fibers, short and continuous. The aim of the study is also to extend the knowledge of the production of composite materials with a defined structure from the point of view of their influence on the microstructure and their physical-mechanical properties.

As part of the experiment, four types of samples were prepared, namely, two types of samples with PA polymer matrix and two types with PET-G polymer matrix. All types contained short carbon fibers and always one set from each polymer matrix in addition to continuous carbon fibers. All types were prepared using the same 3D printing parameters to avoid any further influence. The samples were then tested for microstructure using microCT, mechanical properties using a tensile test and dilatation characteristics from the point of view of aerospace applications. Finally, the raw materials themselves were tested.

The paper provides insight into the influence of polymer matrix types on the physico-mechanical properties of 3D printed composites. The analysis confirmed that the physico-mechanical results varied with respect to the interface between the polymer matrix and the carbon fiber. The implications of the conclusions can be extended to the development of products in the aerospace and automotive sectors.

This study provides information for composite applications in the aerospace industry, focusing on evaluating dilatation characteristics within very low temperatures (−60 °C) when using carbon fibers (continuous carbon fibers, short carbon fibers and a combination of both) in two types of thermoplastic matrices. This perspective on materials characterisation for aerospace applications is a very important and unpublished approach within the 3D printing of composites. These characteristics are important parameters in the design of prototypes and functional samples with regard to the resulting behaviour in real conditions.

This study aims to study the simultaneous treatment of polyethylene terephthalate (PET) fabric with sodium hydroxide (NaOH) and TiO₂ nanoparticles (NPs).

PET fabrics loaded by TiO₂ NPs were investigated by the use of scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and Fourier transformed infrared spectroscopy (FT-IR). Factors affecting the finishing process such as NaOH and TiO₂ NPs concentrations, finishing duration and temperature were discussed.

The finished PET fabrics imparted new properties such as antimicrobial and ultraviolet protection factor protection, what is undoubtedly will increase the spread of this type of fabric and its use in new areas.

The method used mainly depends on activating the surface of PET fabrics by a chemical method, specifically NaOH to cause partial decomposition, which may lead to an environmental impact.

The obtained results revealed that the simultaneous treatment of PET fabric with NaOH and TiO₂ NPs showed antimicrobial and UV protection properties. They exhibited a strong antimicrobial activity and UV protection efficiency even after five washing cycles, indicating excellent laundering durability.

The approach has simplicity and implementability on an industrial scale without cost investment.

This paper aims to extracted sericin from the cocoons of Bombyx mori silkworms, and sericin powder was applied onto drawn textured polyethylene terephthalate (PET) yarns as a spin finish. The reactivity on the surface of PET yarns was analyzed through Fourier transform infrared spectrophotometry–attenuated total reflectance (FTIR-ATR) and dyeing with methylene blue as a reactive dye. Also, investigations were conducted on the effects of sericin, citrc acid (CA) (as a crosslinking agent), and sodium hypophosphite (as a catalyst) concentrations on some properties of false-twist textured PET yarns.

A false-twist texturing machine (Scragg-Shirley minibulk, England) was used with the draw ratio of 1.05, heating temperature of 120°C, texturing speed of 100 m min⁻¹ and applied twist of 3,000 TPM. The aqueous extraction of sericin was carried out by the boiling of the raw silk in distilled water with L:R: 40:1 for 120 min. The aqueous solution was filtered with a filter paper to remove the impurities and insoluble fibroin. Finally, the sericin solution was freeze-dried to obtain the sericin powder. The sericin solution was applied on the drawn textured PET yarns using the “pad-dry-cure” method.

Sericin fixation onto the PET yarns was confirmed by FTIR-ATR. The results showed that there were no significant changes in the tensile strength, linear density, crimp contraction and crimp modulus, elongation at break and shrinkage. In contrast, a substantial increase was observed in moisture regain, vertical wicking, dye uptake and ultraviolet protection. There was also a reduction just in the electrical resistivity, in the presence of sericin.

Although sericin has been known to have numerous beneficial properties, its application in textile industry as a spin finish has not been reported yet.

The use of waste polyethylene terephthalate (PET) plastics derived from shredded bottles in concrete is not formalized yet, especially in reinforced members such as beams and columns. The disposal of plastic wastes in concrete is a viable alternative to manage those wastes while minimizing the environmental impacts associated to recycling, carbon dioxide emissions and energy consumption.

This paper evaluates the suitability of 2D deterministic and stochastic finite element (FE) modeling to predict the shear strength behavior of reinforced concrete (RC) beams without stirrups. Different concrete mixtures prepared with 1.5%–4.5% PET additions, by volume, are investigated.

Test results showed that the deterministic and stochastic FE approaches are accurate to assess the maximum load of RC beams at failure and corresponding midspan deflection. However, the crack patterns observed experimentally during the different stages of loading can only be reproduced using the stochastic FE approach. This later method accounts for the concrete heterogeneity due to PET additions, allowing a statistical simulation of the effect of mechanical properties (i.e. compressive strength, tensile strength and Young’s modulus) on the output FE parameters.

Data presented in this paper can be of interest to civil and structural engineers, aiming to predict the failure mechanisms of RC beams containing plastic wastes, while minimizing the experimental time and resources needed to estimate the variability effect of concrete properties on the performance of such structures.