This paper aims to solve the problems molybdenum disulfide (MoS₂) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.

MoS₂/C₆₀ nanocomposites were prepared by synthesizing molybdenum disulfide (MoS₂) nanosheets on the surface of hydrochloric acid-activated fullerenes (C₆₀) by in situ hydrothermal method. The composition, structure and morphology of MoS₂/C₆₀ nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.

MoS₂/C₆₀ nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS₂/C₆₀ was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.

MoS₂/C₆₀ composite nanoparticles were prepared by in-situ formation of MoS₂ nanosheets on the surface of C₆₀ activated by HCl through hydrothermal method and were used as potential lubricating oil additives.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-10-2023-0321/

Smart contracts are written in high-level programming languages, compiled into Ethereum Virtual Machine (EVM) bytecode, deployed onto blockchain systems and called with the corresponding address by transactions. The deployed smart contracts are immutable, even if there are bugs or vulnerabilities. Therefore, it is critical to verify smart contracts before deployment. This paper aims to help developers effectively and efficiently locate potential defects in smart contracts.

GethReplayer, a smart contract testing method based on transaction replay, is proposed. It constructs a parallel transaction execution environment with two virtual machines to compare the execution results. It uses the real existing transaction data on Ethereum and the source code of the tested smart contacts as inputs, conditionally substitutes the bytecode of the tested smart contract input into the testing EVM, and then monitors the environmental information to check the correctness of the contract.

Experiments verified that the proposed method is effective in smart contract testing. Virtual environmental information has a significant effect on the success of transaction replay, which is the basis for the performance of the method. The efficiency of error locating was approximately 14 times faster with the proposed method than without. In addition, the proposed method supports gas consumption analysis.

This paper addresses the difficulty that developers encounter in testing smart contracts before deployment and focuses on helping develop smart contracts with as few defects as possible. GethReplayer is expected to be an alternative solution for smart contract testing and provide inspiration for further research.

This paper aims to use an ionic liquid (IL, [HMIM]PF₆) to improve the lubrication performance of liquid metal (LM) as a lithium grease additive and to expand the application range of LM.

In this paper, the different mass ratios of [HMIM]PF₆/LM mixtures were added into the lithium grease on a four-ball tribo-meter to investigate the effects of its tribological behavior. Scanning electron mircoscope/energy dispersive spectroscopy and X-ray photoelectron spectroscopy were used to reveal the anti-wear and friction-reducing mechanism of the additives.

When the load was used at 461 N, the average coefficient of friction (ACOF) and average wear scar diameter (AWSD) of steel ball Lubricated with grease with an optimal ratio of 2:3 ([HMIM]PF₆/LM) were reduced by 32.8% and 30.5%, respectively. Friction and wear mechanisms are ascribed to friction-induced additive components that can simultaneously form a composite lubrication film consisting of FePO₄, FeF₃, Ga₂O₃, In₂O₃ and SnO₂.

Compared with the pure lithium-based grease, when [HMIM]PF₆/LM was added with an optimal ratio of 2:3, the ACOF and AWSD were reduced by 12.4% from 0.097 to 0.085 and 23.8% from 552.117 µm to 420.590 µm under 392 N, respectively. When at 461 N, the ACOF and AWSD of steel ball were reduced by 32.8% from 0.122 to 0.082 and 30.5% from 715.714 µm to 497.472 µm, respectively. It was shown that the simultaneous addition of LM and [HMIM]PF₆ can form a composite lubrication film consisting of FePO₄, FeF₃, Ga₂O₃, In₂O₃ and SnO₂.

In this paper, [HMIM]P F₆ is added with LM simultaneously to improve the lubrication properties of lithium grease, and expand the application scope of LM.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2024-0017/