Thermal Fatigue Behaviour of Low Melting Point Solder Joints

Abstract

An empirical study was conducted to determine the thermal fatigue behaviour of 1.27 mm pitch, J‐bend and gullwing surface mount solder joints, manufactured with four low‐temperature solders. Selected solder alloys were: 58Bi‐42Sn (wt %), 43Sn‐43Pb‐14Bi, 52ln‐48Sn and 40ln‐40Sn‐20Pb. Accelerated thermal cycling was used in conjunction with metallographic analysis and mechanical (pull) strength measurement to test their behaviour. The relative merit of each solder composition was determined by comparing it with 63Sn‐37Pb solder, subjected to identical testing conditions. The strength decreased linearly with increased number of thermal cycles for gullwing solder joints of all four solder alloys. The fatigue lifetime was relatively longer for 58Bi‐42Sn and 40ln‐40Sn‐20Pb than for other alloys, but significantly lower than that obtained with 63Sn‐37Pb solder. No discernible degradation of strength was observed with the J‐bend solder joints of any solder alloy, even after the completion of 6000 thermal cycles. Thermal fatigue resistance of the latter joints was attributed to a more favourable coefficient of thermal expansion (CTE) mismatch. Solder joint cracking occurred only in gullwing components soldered with 52ln‐48Sn, 40ln‐40Sn‐20Pb and 43Sn‐43Pb‐14Bi alloys, after 1000 or 2000 thermal cycles. The crack initiated on the outside surface of the solder fillet, and appeared to propagate through both phases of the microstructure. The stress‐induced heterogeneous coarsening of the microstructure was evident only with 43Sn‐43Pb‐14Bi solder, although not as prevalent as that usually observed with eutectic Sn‐Pb solder. Fatigue cracks were absent from solder joints of 58Bi‐42Sn and 63Sn‐37Pb alloys.

Citation

Seyyedi, J. (1993), "Thermal Fatigue Behaviour of Low Melting Point Solder Joints", Soldering & Surface Mount Technology, Vol. 5 No. 1, pp. 26-32. https://doi.org/10.1108/eb037812