Influence of acid hydrolysis on properties of maize starch adhesive

Abstract

Purpose

The purpose of this paper is to obtain high-solids-content and low-viscosity starch adhesive, and improve bonding strength of the pure starch adhesive.

Design/methodology/approach

Maize starch was treated by hydrochloric acid solution with different concentrations, and acid-thinned starch adhesive was prepared. Polyisocyanate as a crosslinking agent was added to improve water resistance of the pure starch adhesive.

Findings

The physical and chemical properties of the acid-thinned starch adhesive were characterised. Acid hydrolysis did not change structure of starch granules, but increased its crystallinity. After acid modification, starch granules became less smooth and some fragments appeared. Acid treatment had little influence on thermal stability of starch, when acid hydrolysis was not strong. High concentration of HCl solution led to starch granules being destroyed, resulting in decrease in bonding strength. The optimal HCl concentration was 0.5 mol/L. Polyisocyanate addition was beneficial to improve the bonding strength of the acid-thinned starch adhesive.

Research limitations/implications

Acid hydrolysis changed the properties of the starch adhesive.

Practical implications

Acid hydrolysis decreased viscosity of the starch adhesive and improved its solids content, which had a positive effect on the application of the starch adhesive.

Social implications

It was helpful to develop an environment-friendly, natural polymer-based wood adhesive.

Originality/value

The properties of acid-thinned starch and acid-thinned starch adhesive were studied.

Citation

Qiao, Z., Lv, S., Gu, J., Tan, H., Shi, J. and Zhang, Y. (2017), "Influence of acid hydrolysis on properties of maize starch adhesive", Pigment & Resin Technology, Vol. 46 No. 2, pp. 148-155. https://doi.org/10.1108/PRT-10-2015-0105