Friction and wear behavior of single-phase high-entropy alloy FeCoNiCrMn under MoS₂-oil lubrication

Abstract

Purpose

The face-centered cubic structured single-phase FeCoNiCrMn high-entropy alloys (HEAs) were prepared to study the friction and wear behavior of HEAs under MoS₂-oil lubrication.

Design/methodology/approach

FeCoNiCrMn alloys were subjected to ball-on-disc reciprocating sliding against the GCr15 ball. L₂₅(5⁶) orthogonal wear tests were designed for velocity V_rel (4.167-20.833 mm/s), load F_N (10-50 N), temperature T (RT-140 °C) and time t (5-20 min). Based on orthogonal test results, multivariate repeated measures ANOVA was performed, and further comparative experiments were conducted for V_rel, F_N and T. Energy dispersive spectrometer and scanning electron microscope were applied to characterize the surface morphology of wear scar and its element distribution.

Findings

V_rel, F_N and t exerted the most significant influence (p < 0.01) on the average friction coefficient f. V_rel and F_N were identified as the momentous effect (p < 0.01) on wear volume ΔV. T (≥50 °C) had positive correlation with f and ΔV, and both V_rel and F_N correlated negatively with f. The dominant abrasive wear was attributed to the large hardness difference of the friction pair. Fatigue wear and delamination wear were experienced at higher speeds (V_rel  ≥ 12.5 mm/s) and loading levels (F_N ≥ 40 N). Elevated temperature weakens the lubrication effect of MoS₂-oil and the mechanical properties of FeCoNiCrMn matrix, intensifying abrasive wear.

Originality/value

This study is expected to provide references for exploration on the wear behavior of single-phase HEAs under complex working conditions with lubrication and hence will help develop the application of HEAs in practical engineering.