The major problem that limits the widespread use of WAAM technology is the forming quality. However, most of the current research focuses on post-process detections that are time-consuming, expensive and destructive. This paper aims to achieve the on-line detection and classification of the common defects, including hump, deposition collapse, deviation, internal pore and surface slag inclusion.

This paper proposes an in-process multi-feature data fusion nondestructive testing method based on the temperature field of the WAAM process. A thermal imager is used to collect the temperature data of the deposition layer in real-time. Efficient processing methods are proposed in this paper, such as the temperature stack algorithm, width extraction algorithm and a classification model based on a residual neural network. Some features closely related to the forming quality were extracted, containing the profile image and width curve of the deposition layer and abnormal temperature features in longitudinal and cross-sections. These features are used to achieve the detection and classification of defects.

Thermal non-destructive testing is a potentially superior technology for in-process detection in the industrial field. Based on the temperature field, extracting the most relevant features of the defect information is crucial. This paper pushes current infrared (IR) monitoring methods toward real-time detection and proposes an in-process multi-feature data fusion non-destructive testing method based on the temperature field of the WAAM process.

In this paper, the single-layer and multi-layer WAAM samples are preset with various defects, such as hump, deposition collapse, deviation, pore and slag inclusion. A multi-feature nondestructive testing methodology is proposed to realize the in-process detection and classification of the defects. A temperature stack algorithm is proposed, which improves the detection accuracy of profile change and solves the problem of uneven temperature from arc striking to arc extinguishing. The combination of residual neural network greatly improves the accuracy and efficiency of detection.

This paper aims to summarize the influence law of hybrid deposited and micro-rolling (HDMR) technology on the bead morphology and overlapping coefficient. A better bead topology positively supports the overlapping deposited in multi-beads between layers while actively assisting the subsequent layer's deposition in the wire and arc additive manufacturing (WAAM). Hybrid-deposited and micro-rolling (HDMR) additive manufacturing (AM) technology can smooth the weld bead for improved surface quality. However, the micro-rolling process will change the weld bead profile fitting curve to affect the overlapping coefficient.

Weld bead contours for WAAM and HDMR were extracted using line lasers. A comparison of bead profile curves was conducted to determine the influence law of micro-zone rolling on the welding bead contour and fitting curve. Aiming at the optimized overlapping coefficient of weld bead in HDMR AM, the optimal HDMR overlapping coefficient curve was proposed which varies with the reduction based on the best surface flatness. The mathematical model for overlapping in HDMR was checked by comparing the HDMR weld bead contours under different rolling reductions.

A fitting function of the bead forming by HDMR AM was proposed based on the law of conservation of mass. The change rule of the HDMR weld bead overlapping spacing with the degree of weld bead rolling reduction was generated using the flat-top transition calculation for this model. Considering the damming-up impact of the first bead, the overlapping coefficient was examined for its effect on layer surface flatness.

Using the predicted overlapping model, the optimal overlapping coefficients for different rolling reductions can be achieved without experiments. These conclusions can encourage the development of HDMR technology.

The study aims to fabricate large metal components with overhangs built on cylindrical or conical surfaces with a high dimensional precision. It proposes methods to address the problems of generating tool-paths on cylindrical or conical surfaces simply and precisely, and planning the welding process on these developable surfaces.

The paper presents the algorithm of tool-paths planning on conical surfaces using a parametric slicing equation and a spatial mapping method and deduces the algorithm of five-axis transformation by addressing the rotating question of two sequential points. The welding process is investigated with a regression fitting model on a flat surface, and experimented on a conical surface, which can be flattened onto a flat surface.

The paper provides slicing and path-mapping expressions for cylindrical and conical surfaces and a curvature-speed-width (CSW) model for wire and arc additive manufacturing to improve the surface appearances. The path-planning method and CSW model can be applied in the five-axis fabrication of the prototype of an underwater thruster. The CSW model has a confidence coefficient of 98.02% and root mean squared error of 0.2777 mm. The reverse measuring of the finished blades shows the residual deformation: an average positive deformation of about 0.5546 mm on one side of the blades and an average negative deformation of about −0.4718 mm on the other side.

Because of the chosen research approach, the research results may lack generalizability for the fabrication based on arbitrary surfaces.

This paper presented an integrated slicing, tool-path planning and welding process planning method for five-axis wire and arc additive manufacturing.

The use of a gas metal arc welding-based weld-deposition, referred to as wire-direct energy deposition or wire-arc additive manufacturing, is one of the notable additive manufacturing methods for producing metallic components at high deposition rates. In this method, the near-net shape is manufactured through layer-by-layer weld-deposition on a substrate. However, as a result of this sequential weld-deposition, different layers are subjected to different types of thermal cycles and partial re-melting. The resulting microstructural evolution of the material may not be uniform. Hence, the purpose of this study is to assess microstructure variation along with the lamination direction (or build direction).

The study was carried out for two different boundary conditions, namely, isolated condition and cooled condition. The microstructural evolution across the layers is hypothesized based on experimental assessment; this included microhardness, scanning electron microscopy imaging and electron backscatter diffraction analysis. These conditions subsequently collaborated with the help of thermal modeling of the process.

During a new layer deposition, the previous layer also is subject to re-melt. While the newly added layer undergoes rapid cooling through a combination of convection, conduction and radiation losses, the penultimate layer, sees a slower cooling curve due to its smaller exposure area. This behavior of rapid-solidification and subsequent re-melting and re-solidification is a progressing phenomenon across the layers and the bulk of the layers have uniform grains due to this remelt-re-solidification phenomenon.

This paper studies the microstructure variation along with the build direction for thin-walled components fabricated through weld-deposition. This study would be helpful in addressing the issue of anisotropy resulting from the distinctive thermal history of each layer in the overall theme of metal additive manufacturing.

The unique aspect of this paper is the postulation of a generic hypothesis, based on experimental findings and supported by thermal modeling of the process, for remelt-re-solidification phenomenon followed by temperature raising/lowering repetitively in every layer deposition across the layers. This is implemented for different types of base plate conditions, revealing the role of boundary conditions on the microstructure evolution.

The modeling and optimization of a weld bead in the middle of the weld are often simple, as the forming process is dynamically balanced. However, the arc striking (AS) and arc extinguishing (AE) areas of weld beads are generally abnormal because the dynamic processes at these areas are unstable. The purpose of this paper is to investigate the abnormal areas of the weld bead with optimization modeling methods in wire and arc additive manufacturing (WAAM).

A burning-back method was proposed to fill the slanted plane in the AE area. To optimize the welding parameters and obtain the optimal design, a response surface methodology was proposed to build the relationships between the input parameters and response variables.

The proposed burning-back method could fill the slanted plane in the AE area. Second-order models of abnormal areas were developed and the optimization effects were analyzed. The experimental results indicated that the relationship models at both ends were applicable and preferable for the optimization of weld beads.

In this paper, a burning-back method was proposed to optimize the slanted plane in the AE area. Second-order models of abnormal areas were established. The methods and models were preferable in the optimization of the abnormal areas in WAAM.

The purpose of this study is to restore the spatial distribution of overseas remittance businesses in Shantou during the 1940s. It explores various socioeconomic factors that influenced the concentration of local remittance business investment in real estate. By reconstructing the spatial distribution of remittance business activities in Shantou, this study hopes to lay a foundation for further analysis of the business strategies of Chaoshan merchants.

This research draws on information from the published Swatow Guide, archival sources and cadastral maps to identify the location of remittance enterprises and the native place and overseas networks of property owners.

This study reveals that the spatial distribution of the remittance enterprises was determined by the native place origins of local property owners, and that the inflow of overseas Chinese capital contributed to real estate development in Shantou.

Despite the limited access to Chinese official archives, this paper manages to identify several building blocks and neighbors in Shantou for spatial analysis.

This study is the first attempt to use the geographical information system (GIS) method in Chinese urban history research and hopes to establish a larger historical database of Shantou as a sample for comparison.

This investigation advances the spatial study of urban history and overseas Chinese remittances in the maritime society of South China.