The purpose of this paper is to evaluate the influence of assembly parameters on lead-free solder joints reliability in Package-on-Package (PoP) Technology and demonstrate factors important for this issue.

Two types of soldering materials and three different assembly procedures were used for assembly of PoP system. The reliability properties of assembled PoP systems were investigated using accelerated aging and periodic resistance measurements of daisy-chain solder joints systems. The purpose of such approach was to determine which soldering material (flux or solder paste) as well as which assembly process parameter (dipping depth of upper component in soldering material), would provide better reliability properties of the solder joints in the PoP system.

It was stated that both selected flux and solder paste dedicated to assembly of PoP systems can be utilized in soldering of PoP applications. More reliable PoP systems applications require larger attention regarding materials selection and assembly parameters. It is recommended 50 per cent dipping depth of ball’s height into soldering material during upper PoP component assembly for more reliable applications. For less demanding PoP systems, the process window from 30 up to 70 per cent is acceptable. All observed failures after thermal shocks occurred in upper PoP components.

This paper explains how materials and assembly parameters have influence on lead-free solder joints reliability in PoP systems. Especially, influence of process window for dipping procedure of upper components balls into soldering material was presented.

The purpose of this paper is to present challenges met during package-on-package (PoP) technology implementation in real surface-mount technology assembly processes.

The properties and behavior of different combinations of soldering materials, PoP components and soldering profiles were investigated, both in the laboratory and during production trials. The purpose of such an approach was identification of existing problems and challenges in lead-free PoP systems assembly as well as checking which soldering material designed to PoP is more suitable for this technology.

Technological trials are needed to select adequate soldering materials for PoP systems assembly, as laboratory tests of materials alone were not sufficient. The challenges of PoP technology were associated with the equipment utilized, the soldering materials, operational parameters and the soldering profile used for assembly. The localization of defects in PoP systems is very difficult and, in many cases, destructive methods have to be used on solder joints for the assessment and confirmation of failures.

This paper shows main materials and soldering challenges in lead-free PoP technology. In particular, the problem related with selection of soldering materials and soldering profiles for PoP was presented. Moreover, the issues that have to be taken into consideration during the planning of a PoP system assembly procedure are presented.

The purpose of this paper is to evaluate the influence of solder powders sizes applied in soldering materials used for Package-on-Package (PoP) system manufacture as well as other factors on reliability and mechanical strength of created solder joints in three-dimensional (3D) PoP structures.

The design of experiments based on the Genichi Taguchi method were used in the investigation. The main factors covered different printed circuit board (PCB) coatings, soldering materials with solder powders sizes from Types 3 to 7 and soldering profiles. The reliability of 3D PoP structures was determined by measurements of resistance of daisy-chain solder joints systems during thermal shocks (TS) cycles. The mechanical strength of solder joints in 3D PoP structures was determined by measurements of a shear force of “Top” layer of 3D structures at T0 and after 1,500 TS. The ANOVA was used for results assessment.

The size of solder powders applied in soldering materials had small (10 per cent) influence on mechanical strength of solder joints in 3D PoP structures. Small size of solder powder had positive effect on solder joints reliability in 3D PoP structures. Especially important was the selection of solder paste for “Bottom” layer of 3D PoP system (influence 17 per cent). Incorrect soldering profile (influence 46 per cent) or wrong selected PCB coating (influence 35 per cent) can very easily reduce the positive impact of soldering materials on solder joints reliability. It was stated that as low as possible soldering profile and organic solderability preservative (OSP) coating in the case of single-sided PCB are the best for 3D PoP structures due to their reliability.

This paper explains how different sizes of solder powders used nowadays in solder pastes influence on reliability and mechanical strength of the solder joints in 3D PoP structures. The contribution, in numerical values, of soldering materials, soldering profile and PCB coating on 3D PoP structures solder joints reliability as well as recommendations improving reliability of 3D PoP structures solder joints were presented.

The purpose of this paper is to investigate the behavior of embedded passives under changing temperature conditions. Influence of different temperature changes on the basic properties of embedded passives was analyzed. The main reason for these investigations was to determine functionality of passives for space application.

The investigations were based on the thin-film resistors made of Ni-P alloy, thick-film resistors made of carbon or carbon-silver inks, embedded capacitors made of FaradFlex materials and embedded inductor made in various configurations. Prepared samples were examined under the influence of a constant elevated temperature (100, 130 or 160°C) in a long period of time (minimum of 30 h), thermal cycles (from −40 to +85°C) or thermal shocks (from −40 to +105°C or from −40 to +125°C).

The achieved results revealed that resistance drift became bigger when the samples were treated at a higher constant temperature. At the same time, no significant difference in change in electrical properties for 50 and 100 Ω resistors was noticed. For all the tests, resistance change was below 2 per cent regardless of a value of the tested resistors. Conducted thermal shock studies indicate that thin-film resistors, coils and some thick-film resistors are characterized by minor variations in basic parameters. Some of the inks may show considerable resistance variations with temperature changes. Significant changes were also exhibited by embedded capacitors.

The knowledge about the behavior of the operating parameters of embedded components considering environmental conditions allow for development of more complex systems with integrated printed circuit boards.