Article
Publication date: 2 September 2014

Ugur Ozsarac, Salim Aslanlar, Faruk Varol and Mehmet Ekici

The purpose of this study was to investigate wear behaviours of brake pads produced from carbon–carbon (C/C) composites in both wet and dry friction sliding conditions. Carbon is…

861

Abstract

Purpose

The purpose of this study was to investigate wear behaviours of brake pads produced from carbon–carbon (C/C) composites in both wet and dry friction sliding conditions. Carbon is probably the most remarkable element in science and also C/C composites are a family of advanced composite materials. They are the most advanced form of carbon and consist of fibre based on carbon precursors embedded in a carbon matrix. In the present work, wear test specimens were prepared according to the related standards and they were exposed to pin-on-disc wear testing in wet and dry sliding conditions with different loads as 10, 20, 30 and 40 N with 1 m/s constant sliding speed. Wet friction process was conducted on all specimens by means of rain water collected from the nature.

Design/methodology/approach

Pin-on-disc wear test tribology lubrication was used.

Findings

Mechanical and physical property measurements of C/C composite brake pad materials: hardness, modulus of elasticity, density and water absorption capacity. Wear performance of materials were measured as coefficient of friction, volumetric loss and specific wear rate.

Originality/value

C/C composite brake pads are used in railway vehicles. Wear performances of them are very important for safety. In this study, wear behaviours of these materials were investigated not only in dry sliding friction condition but also in wet sliding one. Because safety braking is important in all weather conditions for trains, and we used natural rain water to observe the wet sliding friction behaviour of brake pads. “Water lubrication” is an important aspect mentioned in tribology handbooks.

Details

Industrial Lubrication and Tribology, vol. 66 no. 6
Type: Research Article
ISSN: 0036-8792

Keywords

Access Restricted. View access options
Article
Publication date: 7 March 2008

Ugur Ozsarac and Salim Aslanlar

The aim of this study is to calculate the coefficient of friction of wheel/rail interface in both water lubrication and dry friction conditions.

1092

Abstract

Purpose

The aim of this study is to calculate the coefficient of friction of wheel/rail interface in both water lubrication and dry friction conditions.

Design/methodology/approach

Specimens taken from wheel and rail used in railway transport were exposed to pin‐on‐disc wear testing with 10, 20, 30 and 40 N loads. The disc took the place of the rail and the pin that of the wheel in wear tests, and rain water was fed to the disc/pin interface with a three drops/min speed in wet friction conditions. The coefficient of friction and weight loss values of specimens were determined and types of wear mechanism were characterized.

Findings

It was observed that the friction coefficient decreased in wet sliding experiments, so smaller values were calculated in wet friction conditions than those of dry friction conditions for wheel specimens. However, this decrease was more drastic for rail specimens. Weight and volumetric loss values of rail materials were lower than those of wheel samples.

Originality/value

This study investigates the wet and dry sliding wear characteristics of train wheel‐rail materials.