The present research aims to manage the formulations of pigment-based inks containing aminopropyl/vinyl/silsesquioxane (APSV) as a pigment binding agent for inkjet printing of polyester as a commercial trial for the printing of polyester as a single-step process.

The proposed formulations incorporated APSV by using the mini-emulsion technique at a low relieving temperature under the thermal initiation or UV radiation of vinyl-terminated groups in APSV. In this study, the storage stability of inks with regard to physical properties was broadly examined. Moreover, the color performance, including colorimetric data, color fixation and fastness properties of printed fabrics was evaluated.

The results indicated that the inks containing APSV were formulated and were stable in terms of particle size, dispersion stability, surface tension and viscosity over a period of one month and for four freeze/thaw cycles. APSV successfully fixed the pigment-based inkjet inks on polyester fabric and could achieve a significantly higher color performance and degree of fixation than the formulated inks without APSV.

It could also fulfill all the physical properties of ink prerequisites over storing and eliminating all challenges in improving the performance and utilization of inkjet printing.

APSV can also be used as a pigment binding agent to formulate inks for inkjet printing of polyester fabrics as the authors’ past examination for inkjet printing of polyester fabrics post-treated with APSV.

This study eliminates the noteworthy challenges in formulating the pigment-based inks for textile applications by incorporation of a binder while keeping up the necessary viscosity profile for a specific print head.

This study addressed all the issues arising from the complex nature and very challenging requirements of inkjet inks.

The purpose of this paper is to prepare ultra-violet (UV)-curable inkjet inks for textile printing application. The influence of both type and component ratio of monomer/oligomer on the quality of the desired viscosity range is studied. Moreover, the effect of pigment/resin ratio on the rheological behaviour of the ink has been studied.

Aqueous dispersions of nanoscale organic pigments were prepared through ball milling and ultrasonication. The dispersed pigments were encapsulated into UV-curable resin via miniemulsion technique, using different types and component ratios of monomers and oligomers.

It was found that the monomer/oligomer ratio of 2:3 and the pigment/resin ratio of 2:1 gave the most stable miniemulsion dispersions and provided the most suitable rheological range for inkjet printing inks.

As the rheology of the ink is optimised, most of the problems associated with the jetting process could be avoided.

This method of using UV-curable encapsulated inks eliminates the usage of binders, which are the principal factor for nozzle clogging of the print head. In addition, binders are responsible for the coarse handle of the printed textiles.

The UV-curable inks were viewed as a green technology by the US Environmental Protection Agency.

This method is simple and fast and requires low cost. In addition, it could find numerous applications in surface coating.

Wearing clothes requires specifications for feeling comfortable, derived from the fibres, fabrics and finishing properties. This study aims to deal with the effect of economic blends containing hollow fibres, bamboo and cotton/polyester waste on the mechanical properties of the produced fabrics and the appropriate end use.

This research included two blends: one consisted of cotton/polyester wastes blended with bamboo and the other to which Chorisia fibres were added. Two weft counts 10,6/1 Ne were made from each blend, which were used to produce four fabric samples (S1 Chorisia-free and S2 with Chorisia); additionally, another two samples were dyed that contain Chorisia (S3) from each count. The six samples were tested by Kawabata Evaluation System (KES).

The samples gave a good total hand value (THV) for use as men's winter suits, where the thicker count 6/1, with and without Chorisia had better properties, also both counts 6, 10/1 with dye. The hollow fibres affected the fabrics’ properties, including thickness, shear, bending, thermal conductivity and weight. Both blends had a positive effect on THV.

Cotton/polyester waste, Chorisia and bamboo fibres were tested, and 2% Remazol Yellow GNL dye was used.

The ratio of blending, weft counts and dye affected the fabric’s properties, with consequences for the use of the Kawabata system and its applications.

The fabrics used in this research may be considered to be economical and have good THV.

The study proved the usefulness of fabrics made of two blends. The Chorisia component may be seen as a good alternative to cotton fibres to reduce the cost of producing high-consumption winter suit fabrics.