This work aims to develop a new kind of semicrystalline polymer filament and optimize its printing parameters in the fused deposition modeling process. The purpose of this work also includes producing FDM parts with good ductility.

A new kind of semicrystalline filaments composed of long-chain polyamide (PA)1012 was prepared by controlling screw speed and pulling speed carefully. The optimal printing parameters for PA1012 filaments were explored through investigating dimensional accuracy and bonding strength of FDM parts. Furthermore, the mechanical properties of PA1012 specimens were also evaluated by varying nozzle temperatures and raster angles.

It is found that PA1012 filaments can accommodate for FDM process under suitable printing parameters. The print quality and mechanical properties of FDM parts highly depend on nozzle temperature and bed temperature. Even though higher temperatures facilitate stronger interlayer bonding, FDM parts with excellent tensile strength were obtained at a moderate nozzle temperature. Moreover, a bed temperature well above the glass transition temperature of PA1012 can eliminate shrinkage and distortion of FDM parts. As expected, FDM parts prepared with PA1012 filaments exhibit good ductility.

Results in this work demonstrate that the PA1012 filament allows the production of FDM parts with desired mechanical performance. This indicates the potential for overcoming the dependence on amorphous thermoplastics as a feedstock in the FDM technique. This work also provides insight into the effect of materials properties on the mechanical performance of FDM-printed parts.

This paper seeks to explore the evolution of a third generation mobile communications (3G) industry based on TD‐SCDMA technical standard in China through the lens of network analysis.

The authors argue that inter‐firm alliances help companies gain and integrate internal and external resources and foster technical innovation. The paper analyzes alliance governance structures and governance mechanisms in particular, and shows how they protect and improve network‐based innovation capabilities and competitive advantages during a ten‐year period with the method of social network analysis and case studies.

The authors offer a theoretical model that incorporates cooperation among organizations, the maturity of the industrial chain, and the accumulation of organizational knowledge and social capital.

The paper offers a theoretical model of factors that contributes greatly to the development of technical innovation.

This paper aims to investigate the differences in hot corrosion behavior of the GTD222 superalloy and TiC/GTD222 composite in a mixed salt of 75% Na₂SO₄ and 25% K₂SO₄ at 900°C.

The GTD222 superalloy and TiC/GTD222 nickel-based composite were prepared using selective laser melting (SLM). Subsequently, the hot corrosion behavior of the two alloys was systematically investigated in a salt mixture consisting of 75% Na₂SO₄ and 25% K₂SO₄ (Wt.%) at 900°C.

The TiC/GTD222 composite exhibited better hot corrosion resistance compared to the GTD222 superalloy. First, the addition of alloying elements led to the formation of a protective oxide film on the TiC/GTD222 composites 20 h before hot corrosion. Second, TiC/GTD222 composite corrosion surface has a higher Ti content, after 100 h of hot corrosion, the composite corrosion surface Ti content of 10.8% is more than two times the GTD222 alloy 4% Ti. The Ti and Cr oxides are tightly bonded, effectively resisting the erosion of corrosive elements.

The hot corrosion behavior of GTD222 superalloy and TiC/GTD222 composites prepared by SLM in a mixed salt of 75% Na₂SO₄ and 25% K₂SO₄ was studied for the first time. This study provides insights into the design of high-temperature alloys resistant to hot corrosion.