Surgical gowns should be designed and produced using special techniques to provide barrier properties against potential risks during surgery and healthcare procedures. Ultrasonic…
Abstract
Purpose
Surgical gowns should be designed and produced using special techniques to provide barrier properties against potential risks during surgery and healthcare procedures. Ultrasonic welding is one of these methods used to produce surgical gowns with determined barrier properties. The purpose of this paper is to analyse bond strength and permeability properties of ultrasonically welded nonwoven fabrics and compare them with traditional sewing techniques.
Design/methodology/approach
In this study, ultrasonic welding of nonwovens was performed to demonstrate its use as an assembly method. Performance requirements in the design of surgical gowns were determined. Fabric strengths and bond strengths of ultrasonic-welded and traditionally sewn fabrics were analysed. The performance properties, i.e., bond strength, air and water resistance of the fabrics and the joints obtained by ultrasonic and classical sewing methods were studied.
Findings
As a result, it was found that ultrasonic welding technique is a suitable method for joining layers in surgical gown production bringing the advantages of high water resistance together with acceptable bond strength.
Originality/value
The current study focuses on the use of ultrasonic welding of nonwovens used for disposable protective surgical gowns. Ultrasound welding technique was presented as an alternative to classic assembly methods and ultrasonic welding technology was applied to different fabric combinations simulating different layers in different joining sections of a surgical gown.
Details
Keywords
Gülçin Baysal, Gizem Keleş, Berdan Kalav, F. Seniha Güner and Burçak Karagüzel Kayaoğlu
In this study, it is aimed to synthesize ultraviolet (UV)-curable water-borne polyurethane acrylate (WPUA) binders using different types of polyols (poly (propylene glycol), PPG…
Abstract
Purpose
In this study, it is aimed to synthesize ultraviolet (UV)-curable water-borne polyurethane acrylate (WPUA) binders using different types of polyols (poly (propylene glycol), PPG1000 and PPG2000 and poly (ethylene glycol), PEG1000 and PEG2000) at different molecular weights, DMPA (2,2-bis(hydroxymethyl) propionic acid) at different amounts and isophorone diisocyanate (IPDI) and use for pigment printing on synthetic leather.
Design/methodology/approach
UV-cured films were characterized by Fourier transform infrared spectroscopy (FTIR) and differential scanning calorimeter (DSC). The effect of binder structure on printing performance was determined with hardness, crock fastness, abrasion resistance and color measurements.
Findings
The highest abrasion resistance (60,000 cycles) and crock fastness values (dry crock and wet crock: 3/4) were obtained with binder PEG-C synthesized with PEG2000 and lower DMPA amount of 4.89 wt%; however, PEG-C binder showed lower hardness values. Due to lower urethane groups in PEG-C binder, more flexible films were obtained which imparted good adhesion property to printing film. Synthesized binders provided lower crock fastness and abrasion resistance properties than commercial WPUA binder.
Originality/value
Pigmented formulations including UV-curable water-borne synthesized PUA binder were developed and for the first time applied onto synthetic leather using screen printing method. Within this context, a new environmentally friendly printing method was proposed in this study including binder synthesis in the preparation of printing formulations.