This study aims to assess the design, manufacturing and surgical implantation of three-dimensional (3D) customized implants, including surgical preoperative planning, surgery and postoperative results, for cranioplasty along with zygomatic and orbital floor implants using additive manufacturing (AM) technics for a 23-year-old female who suffered from severe craniomaxillofacial trauma.

The skull biomodel was produced in polyamide while implants were made of Ti-6Al-4V alloy by AM.

The method enabled perfectly fitting implants and anatomical conformance with the craniomaxillofacial defect, providing complete healing for the patient. Surgical planning using a customized 3D polyamide biomodel was effective. This proved to be a powerful tool for medical planning and manufacturing of customized implants, as complete healing and good craniofacial aesthetic results were observed.

Satisfactory surgical procedures, regarding surgery time reduction and good craniofacial aesthetic results, were achieved. Furthermore, the 3D titanium customized implants represented a favorable alternative for the repair of craniomaxillofacial defects.

This paper aims to describe the obtainment of Ti-6Al-4V parts with a hierarchical arrangement of pores by additive manufacturing, aiming at designing orthopedic implants.

The experimental methodology compares microstructural and mechanical properties of Menger pre-fractal sponges of Ti-6Al-4V alloy, manufactured by laser powder bed fusion (LPBF) and electron beam powder bed fusion (EBPBF), with three different porosity volumes. The pore arrangement followed the formation sequence of the Menger sponge, with hierarchical order from 1 to 3.

The LPBF parts presented a martensitic microstructure, while the EBPBF parts presented an α + ß microstructure, independently of its wall thickness. The LPBF parts presented higher mechanical resistance and effective stiffness than the EBPBF parts with similar porosity volume. The stiffness values of the Menger pre-fractal sponges of Ti-6Al-4V alloy, between 4 and 29 GPa, are comparable to those of the cortical bone. Furthermore, the deformation behavior presented by the Menger pre-fractal sponges of Ti-6Al-4V alloy did not follow the Gibson and Ashby model's prediction.

To the best of the authors' knowledge, this is the first study to obtain Menger pre-fractal sponges of Ti-6Al-4V alloy by LPBF and EBPBF. The deformation behavior of the obtained porous parts was contrasted with the Gibson and Ashby model's prediction.