This paper aims to study the effect of different Ni content on the microstructure and properties of Sn-0.7Cu alloy. Then, the spreading area, wetting angle, interface layer thickness and microstructure of the soldering interface was observed and analyzed at different soldering temperatures and times.

Sn-0.7Cu-xNi solder alloy was prepared by a high-frequency induction melting furnace. Then Sn-0.7Cu-xNi alloy was soldered on a Cu substrate at different soldering temperatures and times.

It was found that Ni made the intermetallic compounds in the Sn-0.7Cu solder alloy gradually aggregate and coarsen, and the microstructure was refined. The phase compositions of the solder alloy are mainly composed of the ß-Sn phase and a few intermetallic compounds, Cu₆Sn₅ + (Cu, Ni)₆Sn₅. The maximum value of 12.1 HV is reached when the Ni content is 0.1 Wt.%. When the Ni content is 0.5 Wt.%, the wettability of the solder alloy increases by about 15%, the interface thickness increases by about 8.9% and the scallop-like structure is the most refined. When the soldering time is 10 min and the soldering temperature is 280 °C, the wettability of Sn-0.7Cu-0.2Ni is the best.

It is groundbreaking to combine the change in soldering interface with the soldering industry. The effects of different soldering temperatures and times on the Sn-0.7Cu-xNi alloy were studied. Under the same conditions, Sn-0.7Cu-0.2Ni exhibits better wettability and more stable solder joint stability.