The purpose of this study was to characterize the fiber from Curcuma longa (turmeric) stems. The fiber’s properties were used to assess its potential for textile yarn production.

The natural fiber used in this investigation was extracted from agricultural waste through a cold water-retting process.

The Curcuma longa fiber had a crystallinity of 50%. Cellulose, hemicellulose and lignin were detected in the fibers’ Fourier transform infrared spectra. A Curcuma longa fiber bundle contains several constituent fibers. The fibers exhibited an irregular cross-section, with a variable oval shape for the lumen. The fibers of Curcuma longa averaged 30.22 cm in length. The fineness of the fibers was 6.58 Tex. In this study, Curcuma longa fibers had an 11.30% moisture regain. The tensile strength of the fibers was 19.18 g/Tex. Curcuma longa fibers showed a break elongation of 9.79%. The fiber coefficient of friction was 0.3.

Curcuma longa has characteristics that make it appropriate for industrial uses like spinning. Thus, it is possible to use Curcuma longa fiber as a raw material for textiles.

This study aims to analyse cellulose fibres extracted from the pseudo-stems of Cymbopogon citratus and evaluate their properties in non-woven fabric production.

The water retting method was used for fibre extraction, and intrinsic fibre qualities were examined to assess their suitability for textile applications. A thermal bonding technique, using a hot press machine and polylactic acid powder as a binder, was applied for non-woven fabric development.

The retted fibres had an average length of 156 mm and a fineness value of 5.73 tex. The fibre’s tenacity and elongation values were 1.33 gf/denier and 12.78%, respectively. Fourier transform infrared analysis confirmed the presence of major cellulose components. The fibre’s crystallinity and friction coefficient were 50% and 0.3, respectively. C. citratus fibre exhibited hygroscopic characteristics with a moisture regain of 10.65%. Experimental non-woven fabrics (70% C. citratus fibre, 30% polylactic acid powder) demonstrated consistent weight and thickness, with variations in tensile strength. Moisture regain values for non-woven fabrics were approximately 7.6%.

The features of C. citratus fibre, obtained with the water retting process, exhibited suitability for textile applications. Three experimental non-woven fabrics comprising of C. citratus fibre and polylactic acid powder were produced with three different pressing temperatures. The tensile strength properties of these fabrics were influenced by pressing temperature.

The purpose of this study is to analyse the characteristics of cellulose fibres derived from the pseudo-stems of Curcuma longa and to evaluate the properties of non-woven fabric produced using these fibres.

The fibres were extracted via a decortication method. The acquired intrinsic qualities of the fibres were used to assess the feasibility of using them in textile applications. The thermal bonding approach was used for the development of the non-woven fabric, using a hot press machine with low-melt polyester fibre as a binder.

The mean length of Curcuma longa fibres was determined to be 52.73 cm, with a fineness value of 4.00 tex. The fibres exhibited an uneven cross-sectional morphology, characterized by a diverse range of oval-shaped lumens. The fibre exhibited a tenacity of 1.45 g/denier and an elongation value of 4.30%. The fibres possessed a moisture regain value of 11.30%. The experimental non-woven fabrics had consistent weight and thickness, while exhibiting different properties in terms of tensile strength and air permeability, with Fabric C having the highest tensile strength and the lowest air permeability value.

The features of Curcuma longa fibre, obtained with the decortication process, exhibited suitability for textile applications. Three experimental non-woven fabrics comprising different compositions of Curcuma longa fibre and low-melt polyester fibre were produced. The tensile strength and air permeability properties of these fabrics were influenced by the composition of the fibres.

High-performance wrought aluminum alloys, particularly AA6061, are pivotal in industries like automotive and aerospace due to their exceptional strength and good response to heat treatments. Investment casting offers precision manufacturing for these alloys, because casting AA6061 poses challenges like hot cracking and severe shrinkage during solidification. This study aims to address these issues, enabling crack-free investment casting of AA6061, thereby unlocking the full potential of investment casting for high-performance aluminum alloy components.

Nanotechnology is used to enhance the investment casting process, incorporating a small volume fraction of nanoparticles into the alloy melt. The focus is on widely used aluminum alloy 6061, utilizing rapid investment casting (RIC) for both pure AA6061 and nanotechnology-enhanced AA6061. Microstructural characterization involved X-ray diffraction, optical microscopy, scanning electron microscopy, differential scanning calorimetry and energy dispersive X-ray spectroscopy. Mechanical properties were evaluated through microhardness and tensile testing.

The study reveals the success of nanotechnology-enabled investment casting in traditionally challenging wrought aluminum alloys like AA6061. Achieving crack-free casting, enhanced grain morphology and superior mechanical properties, because the nanoparticles control grain sizes and phase growth, overcoming traditional challenges associated with low cooling rates. This breakthrough underscores nanotechnology's transformative impact on the mechanical integrity and casting quality of high-performance aluminum alloys.

This research contributes originality and value by successfully addressing the struggles in investment casting AA6061. The novel nano-treating approach overcomes solidification defects, showcasing the potential of integrating nanotechnology into rapid investment casting. By mitigating challenges in casting high-performance aluminum alloys, this study paves the way for advancements in manufacturing crack-free, high-quality aluminum alloy components, emphasizing nanotechnology's transformative role in precision casting.