This work aims to investigate the feasibility of recycling waste plastic (polyethylene terephthalate) as a coarse aggregate for producing blended cement concrete modified with fly ash and pond ash.

The low, medium and high controlled strength blended cement concrete modified with varied proportions of fly and pond ashes were produced. Manufactured sand and recycled plastic coarse aggregate (RPCA) replaced normal fine and coarse aggregates. Concrete samples were tested for workability, mechanical and durability characteristics. Microstructural analysis was performed on cement concrete blended with fly and pond ashes and compared to conventional concrete samples.

All concrete mixes showed better flowability with values greater than 200 mm. Besides, the maximum flow time was approximately 8 s. The wet density of blended cement concrete-RPCA-based concretes was approximately 30% lower than that of conventional concrete. The compressive strengths of the controlled strength mix at 7 and 28 days were within the specified ranges. While the conventional concrete had slightly higher permeability, the blended cement concrete-RPCA-based concretes had better thermal resistivity and lower thermal conductivity. The scanning electron microscopy analysis revealed the densification of the microstructure due to the filler effects of fly and pond ashes.

This study establishes the prospects of substituting RPCA with normal coarse aggregate in the production of controlled low-strength blended cement concrete, offering benefits of structural fill concrete, lower permeability and thermal conductivity, higher thermal resistivity and reduced density and shrinkage.

The purpose of this study is to analyse the characteristics of cellulose fibres derived from the pseudo-stems of Curcuma longa and to evaluate the properties of non-woven fabric produced using these fibres.

The fibres were extracted via a decortication method. The acquired intrinsic qualities of the fibres were used to assess the feasibility of using them in textile applications. The thermal bonding approach was used for the development of the non-woven fabric, using a hot press machine with low-melt polyester fibre as a binder.

The mean length of Curcuma longa fibres was determined to be 52.73 cm, with a fineness value of 4.00 tex. The fibres exhibited an uneven cross-sectional morphology, characterized by a diverse range of oval-shaped lumens. The fibre exhibited a tenacity of 1.45 g/denier and an elongation value of 4.30%. The fibres possessed a moisture regain value of 11.30%. The experimental non-woven fabrics had consistent weight and thickness, while exhibiting different properties in terms of tensile strength and air permeability, with Fabric C having the highest tensile strength and the lowest air permeability value.

The features of Curcuma longa fibre, obtained with the decortication process, exhibited suitability for textile applications. Three experimental non-woven fabrics comprising different compositions of Curcuma longa fibre and low-melt polyester fibre were produced. The tensile strength and air permeability properties of these fabrics were influenced by the composition of the fibres.