Optimization of friction stir welding process parameters for AA6063-ETP copper using central composite design

Abstract

Purpose

Recently, several studies have been performed on lap welding of aluminum and copper using friction stir welding (FSW). The formation of intermetallic compounds at the weld interface hampers the weld quality. The use of an intermediate layer of a compatible material during welding reduces the formation of intermetallic compounds. The purpose of this paper is to optimize the FSW process parameters for AA6063-ETP copper weld, using a compatible zinc intermediate filler metal.

Design/methodology/approach

In the present study, a three-level, three-factor central composite design (CCD) has been used to determine the effect of various process parameters, namely, tool rotational speed, tool traverse speed and thickness of inter-filler zinc foil on ultimate tensile strength of the weld. A total of 60 experimental data were fitted in the CCD. The experiments were performed with tool rotational speeds of 1,000, 1,200 and 1,400 rpm each of them with tool traverse speeds of 5, 10 and 15 mm/min. A zinc inter-filler foil of 0.2 and 0.4 mm was also used. The macrograph of the weld surface under different process parameters and the tensile strength of the weld have been investigated.

Findings

The feasibility of joining 3 mm thick AA6063-ETP copper using zinc inter-filler is established. The regression analysis showed a good fit of the experimental data to the second-order polynomial model with a coefficient of determination (R²) value of 0.9759 and model F-value of 240.33. A good agreement between the prediction model and experimental findings validates the reliability of the developed model. The tool rotational speed, tool traverse speed and thickness of inter-filler zinc foil significantly affected the tensile strength of the weld. The optimal conditions found for the weld were, rotational speed of 1,212.83 rpm and traverse speed of 9.63 mm/min and zinc foil thickness is 0.157 mm; by using optimized values, ultimate tensile strength of 122.87 MPa was achieved, from the desirability function.

Originality/value

Aluminium and copper sheets could be joined feasibly using a zinc inter-filler. The maximum tensile strength of joints formed by inter-filler (122.87 MPa) was significantly better as compared to those without using inter-filler (83.78 MPa). The optimum process parameters to achieve maximum tensile strength were found by CCD.

Citation

Panaskar, N. and Terkar, R.P. (2020), "Optimization of friction stir welding process parameters for AA6063-ETP copper using central composite design", World Journal of Engineering, Vol. 17 No. 4, pp. 491-507. https://doi.org/10.1108/WJE-11-2019-0322