Study of the role of aluminium and corrosion mechanism in galvalume coating in the marine atmospheric environment

Abstract

Purpose

This study aims to investigate the role of aluminium (Al) in marine environment and the corrosion mechanism of galvalume coatings by conducting accelerated experiments and data analysis.

Design/methodology/approach

Samples were subjected to accelerated corrosion for 136 days via salt spray tests to simulate the natural conditions of marine environment and consequently accelerate the experiments. Subsequently, the samples were examined using various test methods, such as EDS, scanning electron microscopy (SEM), X-ray diffraction (XRD) and electrochemical impedance spectroscopy (EIS), and the obtained data were analysed.

Findings

Galvalume coatings comprised interdigitated zinc (Zn)-rich and dendritic Al-rich phases. Corrosion was observed to begin with a Zn-rich phase. The primary components of the corrosion product film were Al₂O₃ and Zn₅(OH)₈Cl₂·H₂O. It was confirmed that the role of Al was to form a dense protective film, thereby successfully blocking the entry of corrosive media and protecting the iron substrate.

Originality/value

This study provides a clearer understanding of the corrosion mechanism and kinetics of galvalume coatings in a simulated marine environment. In addition, the role of Al, which is rarely mentioned in the literature, was investigated.

Citation

Wang, S., Liu, Q., Wang, J., Chen, N., Chen, J., Song, J., Zhang, X. and Xiao, K. (2024), "Study of the role of aluminium and corrosion mechanism in galvalume coating in the marine atmospheric environment", Anti-Corrosion Methods and Materials, Vol. 71 No. 3, pp. 286-294. https://doi.org/10.1108/ACMM-08-2023-2889