Local electrochemical corrosion performance of nano-SiC/MAO composite coating on 6061-Al alloy

Abstract

Purpose

The purpose of this paper is to improve the corrosion resistance of the 6061-Al alloy as the battery pack material for electric vehicles, and the nano-SiC/MAO composite coating was prepared.

Design/methodology/approach

The corrosion resistance of coatings was evaluated by the global electrochemical test, and the local electrochemical impedance spectroscopy (LEIS) was used to study the local corrosion mechanism. The laser confocal microscope, scanning electron microscope and X-ray diffractometer (XRD) were used to characterise coatings.

Findings

Results showed that the impedance of nano-SiC/MAO coating was 1–2 times higher than MAO coating, and the main corrosion product was Al(OH)₃. LEIS results showed that the impedance of the nano-SiC/MAO coating was two times higher than the MAO coating. The defective SiC/Micro-arc oxidation coating still had high corrosion resistance compared to the MAO coating.

Originality/value

The physical model of the local corrosion mechanism for SiC/MAO composite coating in “cavity-fracture collapse” mode was proposed.

Citation

Liu, Y., Zhao, J., Yang, X., Gu, Y. and Yang, Z. (2022), "Local electrochemical corrosion performance of nano-SiC/MAO composite coating on 6061-Al alloy", Anti-Corrosion Methods and Materials, Vol. 69 No. 6, pp. 592-602. https://doi.org/10.1108/ACMM-01-2022-2590